Product Overview
A moisture-curing reactive polymer coating formulated from isocyanates and polyethers. Manufactured through high-temperature dehydration and polymerization with hybrid curing agents and plasticizers. When applied, the prepolymer's -NCO groups react with atmospheric moisture to form a seamless, flexible rubberized membrane.
Key Features
-
Ready-to-Use Application
No mixing required - direct application from container
Tolerates damp substrates (≤9% moisture content per ASTM D4263)
Applicable at 30-95% relative humidity
-
Elastomeric Performance
Tensile strength: ≥3.5 MPa | Elongation: ≥400% (ASTM D412)
Temperature range: -40°C to +90°C (EN 14891)
-
Application Efficiency
Achieves 1-3mm dry film thickness in single coat
Zero pinholes/bubbles (ISO 10601 compliant)
-
Superior Adhesion
Bond strength: ≥2.5 MPa to concrete (EN 1542)
Eliminates primer requirement on prepared surfaces
Technical Specifications
| Parameter |
Value |
Standard |
| Cure rate |
24h @ 25°C/50% RH |
ASTM D1640 |
| VOC content |
<50 g/L |
ISO 11890 |
| Hydrostatic resistance |
3 bar/168h |
EN 1928 |
Applications
-
Balconies, podiums, and wet decks
-
Expansion joints and movement zones
-
Water containment structures
-
Below-grade foundations